PROPERTIES |
UNITS |
F57 |
Density
|
g/cm3
|
1.2
|
Flexural Strength at Ambient
|
MPa
lbf/in2 |
165
23,925 |
Flexural Strength at 2000C
|
MPa
|
68
|
4 days @2000C Tested @2000C
|
lbf/in2
|
9,860
|
Flexural Modulus at Ambient
|
GPa
lbf/in2 x 106 |
5.6
0.81 |
Flexural Modulus at 2000C |
GPa |
4.3 |
4 days @2000C Tested @2000C
|
lbf/in2 x 106 |
0.62 |
Compressive Strength
|
MPa
lbf/in2 |
380
55,100 |
Bond Strength
|
KN@ 7.9 thick |
4.6 |
Scar Wear
|
mm |
4.3 |
Coefficient of Thermal Expansion |
106/
|
9 |
Maximum Continuous Operating Temperature
|
0C
|
200
|